66 Preparation Of Liquid Fuel From Polypropylene Waste Using Catalytic Pyrolysis


Abstract:

Polypropylene waste was use to prepare liquid fuel by catalytic pyrolysis. The process was carried out with batch reactor at temperature in between 300 O C to 4500 C by using Zeolite, Zinc oxide, Alumina silicate catalyst. The results from catalytic degradation shows yield of liquid fuel in between 63 to 70 %. The maximum yield 70% of liquid fuel was obtained by using zeolite catalyst. It was observed that using zeolite catalyst higher yield can be obtained at low temperature as compared to pyrolysis without catalyst. Kinematic viscosity, flash point, freezing point, density, specific gravity were determined as per ASTM standard. Catalytic degradation of polypropylene waste cab be use as an one of the most time and energy saving alternative recycling method for preparation of liquid fuel from polypropylene waste.

Keywords: Polypropylene waste, Catalytic degradation, Zeolite, catalyst

 

References:

  • A. K. Panda, R. K. Singh, and D. K. Mishra, “Thermolysis of waste plastics to liquid fuel: a suitable method for plastic waste management and manufacture of value added products: a world prospective,” Renewable and Sustainable Energy Reviews, vol. 14, no. 1, pp. 233-248, 2010.
  • S. A. Dawale, “Use of waste plastic coated aggregates in bituminous road construction”, International journal of advancement in engineering technology, management and applied science, volume 3, issue 6 june 2016, page 118-126
  • S. A. Dawale, International journal on design and manufacturing technology volume 8 no.1, Jan. 2014, page 15-20, “Using nanofiltration and ultrafiltration for thr concentration of Amla (phyllanthus Emblica) juice”.
  • Arun Joshi, Rambir and Rakesh Punia, “Conversion of Plastic wastes into liquid fuel – A Review.” Recent Advances in Bioenergy Research Vol. III, chapter 41, pp.444-454, 2014.
  • A. R. Songip, T. Masuda, H. Kuwahara, and K. Hashimoto, “Test to screen catalysts for reforming heavy oil from waste plastics,” Applied Catalysis B, vol. 2, no. 2-3, pp. 153-164, 1993.
  • G. Manos, A. Garforth, and J. Dwyer, “Catalytic degradation of high-density polyethylene on an ultrastable-Y zeolite. Nature of initial polymer reactions, pattern of formation of gas and liquid products, and temperature effects,” Industrial and Engineering Chemistry Research, vol. 39, no.5,  pp. 1203-1208,  2000.
  • N. S. Akpanudoh, K. Gobin, and G. Manos, “Catalytic degradation of plastic waste to liquid fuel over commercial cracking catalysts: effect of polymer to catalyst ratio/acidity content,” Journal of Molecular Catalysis A, vol. 235, no. 1-2, pp. 67-73, 2005.
  • H. Gulab, M. R. Jan, J. Shah, and G. Manos, “Plastic catalytic pyrolysis to fuels as tertiary polymer recycling method: effect of process conditions,” Journal of Environmental Science and Health, vol. 45, no. 7, pp. 908-915, 2010.